Please note: The colour image is as close a representation that we can provide, please consult the Union Ink Color Guide for the true representation.
Polyester low-bleed plastisols (ATHP) – Series are Union’s ultimate high-opacity, low-bleed plastisols formulated to fight dye migration on the worst bleeding 100% polyester athletic uniforms or other synthetic substrates prone to dye migration. ATHP-Series inks are formulated to provide excellent printing characteristics and are designed for both manual and automatic printing.
Premium Low-Bleed White ATHP1070 offers printers a low-bleed white ink with easier printability, increased whiteness and better post-bleed properties.
All standard colours of ATHP-Series inks contain non-migrating pigments. Which prevent overlapping colours from showing through and migrating into each other. All inks are made with non-migrating pigments. Excellent opacity. Superior bleed resistance. Excellent durability.
Direct print low-bleed series for controlling dye migration on 100% polyester fabrics. Athletic uniforms or any other fabrics prone to dye migration Stencils: Any direct emulsion or capillary film compatible with plastisol inks.
Additives: Polyester low-bleed plastisols are supplied ready to print. Since plastisol inks body up as they sit in the container you should always stir the ink well to determine the actual printing viscosity before adding any reducer. The viscosity of Polyester low-bleed plastisol has been carefully formulated to sit on top of the fabric when printed. Reducing will cause the ink to penetrate into the fabric affecting coverage. Any chemical modification will also diminish the inks bleed resistance.
Never add mineral spirits to any plastisol ink.
Printing Instructions: For the best coverage, bleed resistance and brightest prints, adjust the off-contact distance and squeegee pressure to print the ink layer on top of the printed fabric rather than pushing the ink entirely through it. Also be sure to follow recommended emulsion coating techniques as well as exposure settings.
Curing Instructions: Plastisol inks will not air dry and must be heat cured. Polyester low-bleed plastisols will fully cure and withstand repeated washings when the entire thickness of the ink deposit reaches 300°F (149°C). Be careful ink film temperatures do not exceed 330°F (166°C) as this temperature may facilitate dye migration.
Coverage: High Opacity
After Flash Tack: Decreases with increased mesh
Angle: 10° - 20°
Storage Temperature: 65°F - 95°F (18°C - 35°C)
Caution: Always test this product for curing, adhesion, crocking, opacity, bleed resistance, washability and other specific requirements before using in production. Because of the thick ink deposits required by athletic printers, Polyester Low-Bleed plastisols may require higher dryer temperatures or slower belt speeds for the ink deposit to reach the recommended curing temperature. For 100% polyester fabrics prone to extreme dye migration consider using Union's Barrier Clear PLHE-9040 or Barrier Grey PLHE-1500 as an under base especially when light or white overprint colours are required.
Union Ink does not knowingly add plasticizers containing the phthalates listed and outlined in California Bill 1108, CPSIA HR-4040 and Oeko-tex Standard 100. The plasticizers identified may include di-(2-ethylhexyl) phthalate (DEHP), dibutyl phthalate (DBP), benzyl butyl phthalate (BBP), diisononyl phthalate (DINP), diisodecyl phthalate (DIDP), di-n-octyl phthalate (DnOP), (DIBP) Di-iso-butyl, and (DMP) Dimethylphthalate, including esters of ortho-phthalic acid and are not direct ingredients in the manufacture of our Non-Phthalate Inks. Union Ink does not test the final product for amounts of the aforementioned phthalate plasticizers and esters and encourages all users to conduct testing for their intended use.